CYCOLOY™Resin CH6410

SI

|British

|Metric

|PDF

Americas: COMMERCIAL

CH6410 is a high heat, impact modified PC resin, with nonbrominated, nonchlorinated flame retardant system. Limited colors only.

Property

MECHANICAL

Tensile Stress, yld, Type I, 50 mm/min

640

kgf/cm2

ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min

550

kgf/cm2

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min

5.5

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

88

%

ASTM D 638

Tensile Modulus, 50 mm/min

25900

kgf/cm2

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

970

kgf/cm2

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

26500

kgf/cm2

ASTM D 790

Tensile Stress, yield, 50 mm/min

63

MPa

ISO 527

Tensile Stress, break, 50 mm/min

55

MPa

ISO 527

Tensile Strain, yield, 50 mm/min

5

%

ISO 527

Tensile Strain, break, 50 mm/min

95

%

ISO 527

Tensile Modulus, 1 mm/min

2300

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

90

MPa

ISO 178

Flexural Modulus, 2 mm/min

2400

MPa

ISO 178

Hardness, H358/30

100

MPa

ISO 2039-1

IMPACT

Izod Impact, notched, 23°C

92

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy, 23°C

740

cm-kgf

ASTM D 3763

Izod Impact, notched 80*10*4 +23°C

50

kJ/m2

ISO 180/1A

Izod Impact, notched 80*10*4 0°C

19

kJ/m2

ISO 180/1A

Izod Impact, notched 80*10*4 -30°C

15

kJ/m2

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm

55

kJ/m2

ISO 179/1eA

Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm

15

kJ/m2

ISO 179/1eA

THERMAL

HDT, 0.45 MPa, 3.2 mm, unannealed

127

°C

ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed

118

°C

ASTM D 648

CTE, -40°C to 40°C, flow

7.74E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

5.94E-05

1/°C

ASTM E 831

CTE, 23°C to 60°C, flow

7.E-05

1/°C

ISO 11359-2

CTE, 23°C to 60°C, xflow

7.E-05

1/°C

ISO 11359-2

Ball Pressure Test, 125°C +/- 2°C

PASSES

-

IEC 60695-10-2

Vicat Softening Temp, Rate B/50

134

°C

ISO 306

Vicat Softening Temp, Rate B/120

135

°C

ISO 306

HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm

126

°C

ISO 75/Be

HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm

113

°C

ISO 75/Ae

PHYSICAL

Specific Gravity

1.19

-

ASTM D 792

Mold Shrinkage on Tensile Bar, flow (2) (5)

0.05 - 0.07

%

SABIC Method

Mold Shrinkage, flow, 3.2 mm (5)

0.4 - 0.5

%

SABIC Method

Melt Flow Rate, 260°C/2.16 kgf

6.3

g/10 min

ASTM D 1238

Density

1.2

g/cm3

ISO 1183

Melt Volume Rate, MVR at 260°C/5.0 kg

16

cm3/10 min

ISO 1133

ELECTRICAL

Volume Resistivity

>1.E+15

Ohm-cm

IEC 60093

Surface Resistivity, ROA

>1.E+15

Ohm

IEC 60093

Dielectric Strength, in oil, 3.2 mm

18

kV/mm

IEC 60243-1

Relative Permittivity, 1 MHz

2.7

-

IEC 60250

Dissipation Factor, 50/60 Hz

0.001

-

IEC 60250

Dissipation Factor, 1 MHz

0.01

-

IEC 60250

Comparative Tracking Index

225

V

IEC 60112

Relative Permittivity, 50/60 Hz

2.7

-

IEC 60250

FLAME CHARACTERISTICS

UL Recognized, 94V-1 Flame Class Rating (3)

0.99

mm

UL 94

UL Recognized, 94V-0 Flame Class Rating (3)

1.49

mm

UL 94

Source GMD, last updated:2002/10/29

Processing

Injection Molding

Drying Temperature

90 - 100

°C

Drying Time

2 - 4

hrs

Drying Time (Cumulative)

8

hrs

Maximum Moisture Content

0.04

%

Melt Temperature

270 - 300

°C

Nozzle Temperature

265 - 300

°C

Front - Zone 3 Temperature

265 - 300

°C

Middle - Zone 2 Temperature

260 - 300

°C

Rear - Zone 1 Temperature

260 - 300

°C

Mold Temperature

60 - 90

°C

Back Pressure

0.3 - 0.7

MPa

Screw Speed

40 - 70

rpm

Shot to Cylinder Size

40 - 80

%

Vent Depth

0.038 - 0.076

mm