CYCOLOY™Resin CM6140

SI

|British

|Metric

|PDF

Americas: COMMERCIAL

Cycoloy resin grade CM6140 is a flame retardant, filled PC/ABS blend. It is of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm. Key features include thin wall FR, higher stiffness, balanced properties in flow, impact and heat designed for various thin wall applications.

Property

MECHANICAL

Tensile Stress, yld, Type I, 50 mm/min

660

kgf/cm2

ASTM D 638

Tensile Stress, yld, Type I, 5 mm/min

660

kgf/cm2

ASTM D 638

Tensile Stress, brk, Type I, 5 mm/min

500

kgf/cm2

ASTM D 638

Tensile Strain, yld, Type I, 5 mm/min

4

%

ASTM D 638

Tensile Strain, brk, Type I, 5 mm/min

100

%

ASTM D 638

Tensile Modulus, 5 mm/min

35600

kgf/cm2

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

1010

kgf/cm2

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

33600

kgf/cm2

ASTM D 790

Tensile Stress, break, 5 mm/min

50

MPa

ISO 527

Tensile Strain, yield, 5 mm/min

3.5

%

ISO 527

Tensile Strain, break, 50 mm/min

15

%

ISO 527

Tensile Modulus, 1 mm/min

3200

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

97

MPa

ISO 178

Flexural Modulus, 2 mm/min

3450

MPa

ISO 178

IMPACT

Izod Impact, notched, 23°C

20

cm-kgf/cm

ASTM D 256

Izod Impact, notched, -30°C

8

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy, 23°C

509

cm-kgf

ASTM D 3763

Izod Impact, notched 80*10*3 +23°C

10

kJ/m2

ISO 180/1A

Izod Impact, notched 80*10*3 -30°C

5

kJ/m2

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm

10

kJ/m2

ISO 179/1eA

Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm

5

kJ/m2

ISO 179/1eA

THERMAL

Vicat Softening Temp, Rate B/50

91

°C

ASTM D 1525

HDT, 1.82 MPa, 3.2mm, unannealed

83

°C

ASTM D 648

HDT, 0.45 MPa, 6.4 mm, unannealed

97

°C

ASTM D 648

HDT, 1.82 MPa, 6.4 mm, unannealed

89

°C

ASTM D 648

CTE, -40°C to 40°C, flow

5.5E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

6.E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, flow

5.5E-05

1/°C

ISO 11359-2

CTE, -40°C to 40°C, xflow

6.E-05

1/°C

ISO 11359-2

Ball Pressure Test, 75°C +/- 2°C

PASSES

-

IEC 60695-10-2

Vicat Softening Temp, Rate B/50

98

°C

ISO 306

Vicat Softening Temp, Rate B/120

102

°C

ISO 306

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

80

°C

ISO 75/Af

PHYSICAL

Specific Gravity

1.26

-

ASTM D 792

Water Absorption, 24 hours

0.1

%

ASTM D 570

Moisture Absorption, 50% RH, 24 hrs

0.01

%

ASTM D 570

Mold Shrinkage, flow, 3.2 mm (5)

0.3 - 0.5

%

SABIC Method

Mold Shrinkage, xflow, 3.2 mm (5)

0.4 - 0.6

%

SABIC Method

Melt Flow Rate, 260°C/2.16 kgf

17.5

g/10 min

ASTM D 1238

Density

1.25

g/cm3

ISO 1183

Water Absorption, (23°C/sat)

0.09

%

ISO 62

Moisture Absorption (23°C / 50% RH)

0.01

%

ISO 62

Melt Volume Rate, MVR at 220°C/5.0 kg

14

cm3/10 min

ISO 1133

ELECTRICAL

Volume Resistivity

2.68E+16

Ohm-cm

ASTM D 257

Surface Resistivity

3.54E+15

Ohm

ASTM D 257

FLAME CHARACTERISTICS

UL Recognized, 94V-1 Flame Class Rating (3)

0.6

mm

UL 94

UL Recognized, 94V-0 Flame Class Rating (3)

0.8

mm

UL 94

UL Recognized, 94-5VB Rating (3)

1.5

mm

UL 94

Glow Wire Flammability Index 960°C, passes at

0.8

mm

IEC 60695-2-12

Glow Wire Ignitability Temperature, 1.0 mm

850

°C

IEC 60695-2-13

Glow Wire Ignitability Temperature, 3.0 mm

800

°C

IEC 60695-2-13

Source GMD, last updated:2004/12/02

Processing

Injection Molding

Drying Temperature

90

°C

Drying Time

>4

hrs

Maximum Moisture Content

0.04

%

Melt Temperature

275 - 300

°C

Nozzle Temperature

280 - 300

°C

Front - Zone 3 Temperature

280 - 300

°C

Middle - Zone 2 Temperature

275 - 300

°C

Rear - Zone 1 Temperature

275 - 300

°C

Mold Temperature

60 - 80

°C