型號：Cycoloy PC/ABS CM6210
性能：通用級，PC/ABS，高模量。
|
CYCOLOY™Resin CM6210 | | Americas: COMMERCIAL |
| Cycoloy* resin CM6210 is a high-modulus flame retardant PC/ABS with non-brominated and non-chlorinated FR system. It can be used for extrusion & thermoforming applications and also for injection molding applications where higher stiffness is needed. |
| Property |
| TYPICAL PROPERTIES(1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 5 mm/min | 650 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 500 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 4.9 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 80 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 36400 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1120 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 35600 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 59 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 65 | MPa | ISO 527 | |
| Tensile Stress, yield, 50 mm/min | 63 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 50 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 3.6 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 101 | % | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 3.5 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 97 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 3660 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 106 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 3560 | MPa | ISO 178 | |
| Hardness, Rockwell R | 98 | - | ISO 2039-2 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 50 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, notched, -30°C | 9 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 458 | cm-kgf | ASTM D 3763 | |
| Izod Impact, notched 80*10*3 +23°C | 45 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 10 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 45 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m2 | ISO 179/1eA | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 106 | °C | ASTM D 1525 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 90 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 5.7E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 7.E-05 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.3 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 5.2E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, flow | 5.2E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 75°C +/- 2°C | pass | - | IEC 60695-10-2 | |
| Ball Pressure Test, approximate maximum | 95 | °C | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/50 | 112 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 114 | °C | ISO 306 | |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 99 | °C | ISO 75/Be | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 89 | °C | ISO 75/Ae | |
| Relative Temp Index, Elec | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.28 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.4 - 0.6 | % | SABIC Method | |
| Melt Flow Rate, 260°C/5.0 kgf | 11.5 | g/10 min | ASTM D 1238 | |
| Density | 1.27 | g/cm3 | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.3 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.1 | % | ISO 62 | |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 9 | cm3/10 min | ISO 1133 | |
| ELECTRICAL | Value | Unit | Standard | |
| Dielectric Strength, in oil, 0.8 mm | 38 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 26 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 1 MHz | 2.8 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.003 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.004 | - | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 | |
| Relative Permittivity, 50/60 Hz | 2.9 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 | |
| Source GMD, last updated:2005/02/08 |
| Processing |
| • Barrel temperatures should be banked TO 150°C (300°F) |
| Parameter | ||
| Sheet Extrusion | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Minimum Moisture Content | 0.04 | % |
| Melt Temperature | 220 - 245 | °C |
| Barrel - Zone 1 Temperature | 180 - 225 | °C |
| Barrel - Zone 2 Temperature | 190 - 230 | °C |
| Barrel - Zone 3 Temperature | 205 - 240 | °C |
| Barrel - Zone 4 Temperature | 210 - 245 | °C |
| Adapter Temperature | 210 - 245 | °C |
| Die Temperature | 210 - 245 | °C |
| Roll Stack Temp - Top | 70 - 100 | °C |
| Roll Stack Temp - Middle | 70 - 95 | °C |
| Roll Stack Temp - Bottom | 65 - 90 | °C |