CYCOLOY™Resin CP8320 | SI | |British | |Metric | | Americas: COMMERCIAL |
| Cycoloy Medium Heat Plating Grade for Automotive |
| Property |
| TYPICAL PROPERTIES(1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 50 mm/min | 450 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 400 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 100 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 21400 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 710 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 20300 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, yield, 50 mm/min | 45 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2100 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 65 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 61 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, notched, -30°C | 40 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 560 | cm-kgf | ASTM D 3763 | |
| Izod Impact, notched 80*10*3 +23°C | 60 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 30 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 60 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 30 | kJ/m2 | ISO 179/1eA | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 106 | °C | ASTM D 1525 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 90 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 9.E-05 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow | 9.E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 75°C +/- 2°C | Pass | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/50 | 106 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 107 | °C | ISO 306 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 92 | °C | ISO 75/Af | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.1 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method | |
| Melt Flow Rate, 260°C/5.0 kgf | 14 | g/10 min | ASTM D 1238 | |
| Density | 1.1 | g/cm3 | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.3 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.1 | % | ISO 62 | |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 13 | cm3/10 min | ISO 1133 | |
| ELECTRICAL | Value | Unit | Standard | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm | 35 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm | 25 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 | |
| Source GMD, last updated:2006/06/14 |
| Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 95 - 105 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 280 | °C |
| Nozzle Temperature | 230 - 270 | °C |
| Front - Zone 3 Temperature | 240 - 280 | °C |
| Middle - Zone 2 Temperature | 240 - 280 | °C |
| Rear - Zone 1 Temperature | 220 - 250 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 60 - 90 | °C |