CYCOLOY™Resin CY6310 | | Americas: COMMERCIAL |
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow / impact balance for a wide variety of thin wall or large size applications including business equipment, enclosures, among others. |
Property |
TYPICAL PROPERTIES(1) | ||||
MECHANICAL | Value | Unit | Standard | |
Tensile Stress, yld, Type I, 50 mm/min | 640 | kgf/cm2 | ASTM D 638 | |
Tensile Stress, brk, Type I, 50 mm/min | 500 | kgf/cm2 | ASTM D 638 | |
Tensile Strain, yld, Type I, 50 mm/min | 4.2 | % | ASTM D 638 | |
Tensile Strain, brk, Type I, 50 mm/min | >50 | % | ASTM D 638 | |
Tensile Modulus, 5 mm/min | 27500 | kgf/cm2 | ASTM D 638 | |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1020 | kgf/cm2 | ASTM D 790 | |
Flexural Modulus, 1.3 mm/min, 50 mm span | 27500 | kgf/cm2 | ASTM D 790 | |
Tensile Stress, yield, 50 mm/min | 63 | MPa | ISO 527 | |
Tensile Stress, break, 50 mm/min | 51 | MPa | ISO 527 | |
Tensile Strain, yield, 50 mm/min | 4.4 | % | ISO 527 | |
Tensile Strain, break, 50 mm/min | >50 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 2700 | MPa | ISO 527 | |
Flexural Stress, yield, 2 mm/min | 91 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min | 2650 | MPa | ISO 178 | |
IMPACT | Value | Unit | Standard | |
Izod Impact, notched, 23°C | 61 | cm-kgf/cm | ASTM D 256 | |
Izod Impact, notched, -30°C | 11 | cm-kgf/cm | ASTM D 256 | |
Multiaxial Impact | 1070 | cm-kgf | ISO 6603 | |
Instrumented Impact Total Energy, 23°C | 662 | cm-kgf | ASTM D 3763 | |
Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U | |
Izod Impact, notched 80*10*3 +23°C | 50 | kJ/m2 | ISO 180/1A | |
Izod Impact, notched 80*10*3 -30°C | 13 | kJ/m2 | ISO 180/1A | |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 55 | kJ/m2 | ISO 179/1eA | |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 14 | kJ/m2 | ISO 179/1eA | |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m2 | ISO 179/1eU | |
THERMAL | Value | Unit | Standard | |
Vicat Softening Temp, Rate B/50 | 109 | °C | ASTM D 1525 | |
HDT, 0.45 MPa, 3.2 mm, unannealed | 100 | °C | ASTM D 648 | |
HDT, 1.82 MPa, 3.2mm, unannealed | 88 | °C | ASTM D 648 | |
CTE, -40°C to 40°C, flow | 6.8E-05 | 1/°C | ASTM E 831 | |
CTE, -40°C to 40°C, xflow | 7.E-05 | 1/°C | ASTM E 831 | |
CTE, -40°C to 40°C, flow | 6.8E-05 | 1/°C | ISO 11359-2 | |
CTE, -40°C to 40°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 | |
Ball Pressure Test, 75°C +/- 2°C | Pass | - | IEC 60695-10-2 | |
Ball Pressure Test, approximate maximum | 95 | °C | IEC 60695-10-2 | |
Vicat Softening Temp, Rate B/50 | 109 | °C | ISO 306 | |
Vicat Softening Temp, Rate B/120 | 111 | °C | ISO 306 | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 90 | °C | ISO 75/Af | |
Relative Temp Index, Elec | 85 | °C | UL 746B | |
Relative Temp Index, Mech w/impact | 85 | °C | UL 746B | |
Relative Temp Index, Mech w/o impact | 85 | °C | UL 746B | |
PHYSICAL | Value | Unit | Standard | |
Specific Gravity | 1.16 | - | ASTM D 792 | |
Mold Shrinkage, flow, 3.2 mm (5) | 0.4 - 0.6 | % | SABIC Method | |
Melt Flow Rate, 250°C/2.16 kgf | 16 | g/10 min | ASTM D 1238 | |
Melt Flow Rate, 260°C/2.16 kgf | 20 | g/10 min | ASTM D 1238 | |
Density | 1.16 | g/cm3 | ISO 1183 | |
Water Absorption, (23°C/sat) | 0.6 | % | ISO 62 | |
Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 | |
Melt Volume Rate, MVR at 260°C/2.16 kg | 19 | cm3/10 min | ISO 1133 | |
ELECTRICAL | Value | Unit | Standard | |
Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A | |
High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A | |
Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
Comparative Tracking Index | 575 | V | IEC 60112 | |
FLAME CHARACTERISTICS | Value | Unit | Standard | |
UL Compliant, 94V-2 Flame Class Rating (3)(4) | 0.75 | mm | UL 94 by SABIC-IP | |
UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by SABIC-IP | |
UL Compliant, 94-5VA Rating (3)(4) | 2.9 | mm | UL 94 by SABIC-IP | |
UL Compliant, 94-5VB Rating (3)(4) | 2.3 | mm | UL 94 by SABIC-IP | |
UL Recognized, 94V-2 Flame Class Rating (3) | 0.75 | mm | UL 94 | |
UL Recognized, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 | |
UL Recognized, 94-5VA Rating (3) | 2.9 | mm | UL 94 | |
UL Recognized, 94-5VB Rating (3) | 2.3 | mm | UL 94 | |
Glow Wire Flammability Index 960°C, passes at | 3 | mm | IEC 60695-2-12 | |
Oxygen Index (LOI) | 30 | % | ISO 4589 |
Source GMD, last updated:2007/08/16 |
Processing |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 90 - 100 | °C |
Drying Time | 2 - 4 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 250 - 280 | °C |
Nozzle Temperature | 230 - 270 | °C |
Front - Zone 3 Temperature | 240 - 280 | °C |
Middle - Zone 2 Temperature | 230 - 270 | °C |
Rear - Zone 1 Temperature | 210 - 240 | °C |
Hopper Temperature | 60 - 80 | °C |
Mold Temperature | 60 - 90 | °C |