性能：注塑級，高剛度，PC/ABS混合，高耐熱性，良好的注射成型。
|
CYCOLOY™Resin XCM840 | | Americas: COMMERCIAL |
| High stiffness PC/ABS blend offering practical impact, low CTE, high heat resistance, with good aesthetics suitable for injection molding |
| Property |
| TYPICAL PROPERTIES(1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 5 mm/min | 570 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 470 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 4 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 43800 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, yield, 5 mm/min | 56 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 47 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 4 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 50 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 4300 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 100 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 4000 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Instrumented Impact Total Energy, 23°C | 611 | cm-kgf | ASTM D 3763 | |
| Izod Impact, notched 80*10*3 +23°C | 15 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 8 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 37 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 10 | kJ/m2 | ISO 179/1eA | |
| THERMAL | Value | Unit | Standard | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 120 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 4.6E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 6.1E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 4.6E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.1E-05 | 1/°C | ISO 11359-2 | |
| Vicat Softening Temp, Rate B/50 | 138 | °C | ISO 306 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.27 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method | |
| Mold Shrinkage, xflow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method | |
| Density | 1.27 | g/cm3 | ISO 1183 | |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 10 | cm3/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 12 | cm3/10 min | ISO 1133 | |
| Source GMD, last updated:2013/03/26 |
| Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 125 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.01 | % |
| Melt Temperature | 270 - 300 | °C |
| Nozzle Temperature | 260 - 290 | °C |
| Front - Zone 3 Temperature | 270 - 300 | °C |
| Middle - Zone 2 Temperature | 265 - 290 | °C |
| Rear - Zone 1 Temperature | 260 - 270 | °C |
| Mold Temperature | 60 - 100 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 30 - 80 | % |
| Vent Depth | 0.038 - 0.076 | mm |