型號(hào)：PC/ABS Lexan JK2500
性能：通用級(jí)，Cycoloy PC/ABS，20%碳纖維增強(qiáng)。
|
LNP™STAT-KON™Compound Lexan_JK2500 | | Americas: COMMERCIAL |
| LNP* Stat-kon* Lexan_JK2500 compound is a 20% carbon-fiber reinforced, nonhalogenated red phosporous-free, high-flow FR PC+ABS for EMI/RFI shielding. SE of 21 dB at 1.5 mm. |
| Property |
| TYPICAL PROPERTIES(1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 5 mm/min | 650 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 650 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 2.3 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 2.4 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 112400 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 1140 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 94200 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 63 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 63 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 2.2 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 2.3 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 11130 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 110 | MPa | ISO 178 | |
| Flexural Stress, break, 2 mm/min | 110 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 10090 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23°C | 22 | cm-kgf/cm | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 5 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 149 | cm-kgf | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*4 +23°C | 15 | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 111 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 98 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 93 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 96 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 1.26E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 6.3E-05 | 1/°C | ASTM E 831 | |
| CTE, 23°C to 80°C, flow | 8.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 7.7E-05 | 1/°C | ISO 11359-2 | |
| Vicat Softening Temp, Rate B/120 | 100 | °C | ISO 306 | |
| Relative Temp Index, Elec | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.31 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.06 - 0.15 | % | SABIC Method | |
| Mold Shrinkage, xflow, 3.2 mm (5) | 0.2 - 0.4 | % | SABIC Method | |
| Melt Flow Rate, 300°C/1.2 kgf | 25 | g/10 min | ASTM D 1238 | |
| ELECTRICAL | Value | Unit | Standard | |
| Volume Resistivity | 2.E+00 | Ohm-cm | ASTM D 257 | |
| Surface Resistivity | 1.E+04 | Ohm | ASTM D 257 | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94V-0 Flame Class Rating (3) | 0.99 | mm | UL 94 | |
| Source GMD, last updated:2002/10/29 |
| Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Melt Temperature | 270 - 310 | °C |
| Nozzle Temperature | 270 - 300 | °C |
| Front - Zone 3 Temperature | 270 - 300 | °C |
| Middle - Zone 2 Temperature | 270 - 290 | °C |
| Rear - Zone 1 Temperature | 260 - 275 | °C |
| Mold Temperature | 50 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 35 - 75 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.038 - 0.076 | mm |