高粘度 擠出級 PBT/D3200LC
Celanese Celanex®6035GB20 PBT, 20% Glass Bead Filled
Celanese Celanex® 6406PBT, 40% Mineral / Glass Reinforced
Celanese Celanex® 6407HRPBT, 30% Mineral / Glass Reinforced
Celanese Celanex® 6500HFPBT, Mineral / Glass Reinforced
Celanese Celanex® 6500HRPBT, Mineral / Glass Reinforced
Celanese Celanex® 6500LMPBT, 30% Mineral / Glass Reinforced
Celanese Celanex® 7316PBT, 35% Mineral / Glass Reinforced
Celanese Celanex® 7407PBT, 40% Glass Reinforced
Celanese Celanex® 7714PBT, Mineral / Glass Reinforced
Celanese Celanex® D3200LCPBT, Unfilled
Celanese Celanex® J235PBT, 35% Mineral / Glass Reinforced
Celanese Celanex® LW2333RPBT, 50% Specialty
Celanese Celanex® LW2547WPBT, 30% Mineral / Glass Reinforced
Celanese Celanex® XFR6842 GF10 PBT, 30% Glass Reinforced
Celanese Celanex® XFR6842 GF20 PBT, 30% Glass Reinforced
Celanese Celanex® 1300APolyester (PBT)
Celanese Celanex® 2002Polyester (PBT)
Celanese Celanex® 2003Polyester (PBT)
Celanese Celanex® 2004Polyester (PBT)
PBT工藝條件
干燥處理:這種材料在高溫下很容易水解,因此加工前的干燥處理是很重要的。建議在空氣中的干燥條件為120℃,6~8小時,或者150℃,2~4小時。濕度必須小于0.03%。如果用吸濕干燥器干燥,建議條件為150℃,2.5小時。[2]
熔化溫度:225~275℃,建議溫度:250℃。
模具溫度:對于未增強(qiáng)型的材料為40~60℃。要很好地設(shè)計模具的冷卻腔道以減小塑件的彎曲。熱量的散失一定要快而均勻。建議模具冷卻腔道的直徑為12mm。
注射壓力:中等(較大到1500bar)。
注射速度:應(yīng)使用盡可能快的注射速度(因為PBT的凝固很快)。
流道和澆口:建議使用圓形流道以增加壓力的傳遞(經(jīng)驗公式:流道直徑=塑件厚度+1.5mm)??梢允褂酶鞣N型式的澆口。也可以使用熱流道,但要注意防止材料的滲漏和降解。澆口直徑應(yīng)該在0.8~1.0*t之間,這里 t是塑件厚度。如果是潛入式澆口,建議小直徑為0.75mm。